There are various route to increase the strength of steel used for construction. One of the oldest route is the CTD Bar route. Here the bars are cold twisted after rolling. Another method is the Micro Alloying of steel to get high strength.
The problem with both these systems is the hogh labour, cost and time. In CTD bars the cost of twisting and this is the main bottleneck in all the mills. For Micro alloying the cost alloying elements is very high.
To counter these problems, SMT has developed High Strength with High Ductility |
| |
TMT Quenched & Tempred Ribbed Bars
of Grade Fe 415 & Fe 500 confirming to IS 1786 |
| |
| We are happy to offer our International Computerized Version with the latest development " Extended Nozzles ". |
 |
| Thus, we have Quenched & Tempered TMT Bars having the following Advantages over CTD Bars |
| High Strength with High Ductility
High Corrosion Resistance
Very High Weld - ability
Very High Bend - ability
High Strength at Elevated Temperature
Bars are Stress Free
Bars have Protective Shield
Pollution Free
Lower Manufacturing Cost
100% depreciation
International Quality Products
Saving in steel
50% Less Labour in Mills etc. |
 |
| |
CHEMISTRY for Quality TMT |
| Billet / Ingot CHEMISTRY: |
| One of the major factor that effect that effect the Quality of TMT is CHEMISTRY. The word GIGO aptly describes the process: |
Gold in Gold out
Also
Garbage in Garbage Out |
| To get good quality TMT ensure that Carbon Equivalent is around 0.38 For our purpose this formula holds good. |
Carbon Equivalent Ce = Carbon C + Managanese Mn/6.
Ce = C+ Mn/6. |
To get good weld - able quality TMT keep Carbon between 0.20 to 0.25
The implication is |
| For Carbon 0.20 Mn = 1.08 |
0.38 = 0.20 + Mn/6
Mn = [0.38 - 0.20] X 6 = 1.08 |
| For Carbon 0.25 Mn = 1.78 |
0.38 = 0.25 + Mn/6
Mn = [0.38 - 0.25] X 6 = 0.78 |
| |
| With this composition we can assure good Quality TMT which has high strength with High Ductility. |
| Remember |
Higher the Carbon, Lower the elongation
with same Carbon Equivalent Ce |
| |
TMT Process is a Quench & Temper Rolling process.
For prefabrication of TMT bars, lower Ce helps. With high Ce the weld - ability of TMT is effected.
Ce above 0.43 is not advisable for weld-able TMT bars.
In -order to get Premium Quality TMT bars with High Strength and High Ductility, Maintain Ce = 0.38 with the following chemistry for TMT bars. |
| |
It is very important to maintain all the elements at the correct percentage.
Any dilution leads to Lowering of Quality and subsequent bar rejection.
|
| |
|
| |
| |
 |
 |
| |